From the point of view of many test results, the softening temperature of the water glass shows that the water-reclamation temperature of the refractory of the water glass generally starts at the heating temperature and then the refractory brick powder is used as a fine grinding admixture. The quartz sand is used as a fine grinding admixture for compression. The temperature is the compression temperature is a load softening temperature and the amount of water glass water glass module sodium fluoride sodium content and the type of aggregate.
When the amount of water glass is, the softening temperature of the load is at the beginning and when the amount of water glass is increased, the softening temperature of the load is correspondingly decreased and the modulus of the water glass is increased. The softening temperature of the water is correspondingly increased, and the proportional relationship is formed. The inorganic silicon compound is cemented and fireproofed. Material application development table load softening temperature starting point compression% after load softening temperature is an important thermal performance of water glass refractories, so in the thermal engineering should not use low modulus water glass.
The effect of aggregate type on the softening temperature of the load The load softening temperature Aggregate name Starting point Compression silica brick Magnesia brick Refractory clay brick Emergency cold water Hot water glass Refractories Good quenching and rapid thermal performance, subject to sub-quenching and rapid heat in the air, The strength is not lower than the drying strength. The effect of three aggregates on the quenching and rapid heat of water glass refractories. The experimental results show that the factors affecting the quenching and rapid heating have little relationship with the water glass dosage modulus and the hardening agent content, and have a great influence on the types of coarse and fine aggregates.
Cooling and rapid thermal performance Alternation of aggregate name in water Number of times of weight loss Alternating strength in water Silica brick Magnesia brick Fireclay brick Test results show that silica brick and magnesium brick water glass refractories have poor quench and heat properties, and fire clay Bricks have good performance, the former only once.
Gabion mattresses are used for river bank and scour protection, channel linings for erosion control, and embankment stability. They are filled with rock at the project site to form flexible, permeable, monolithic structures to promote rapid growth of natural vegetation. The base section of the Gabion Mattress is divided into compartments and filled with stones at the project site. With lids secured, Gabion mattresses form flexible, permeable, monolithic structures.
Features:
Low maintenance.
Simple assembly and filling, no need for qualified labour.
Filling is available in direct proximity.
Foundation work not necessary, only a place surface on a sustainable ground is needed.
Reno Mattress support the natural bank vegetataion and integrates naturally in the surrounding landscape
Packaging Details
1. Nude package,compacted before packaging.
2. Plastic packaging outside and on the pallet.
3 .Customized.according to the customers' requirment.
Reno Mattress
Reno Mattress,Gabion Mattress,Gabion Reno Mattress,Galvanized Reno Mattress Mesh
Anping shengsen metal wire mesh products co,. ltd , https://www.apshengsen.com